熱穩(wěn)定 Ultramid? B3WG6 德國(guó)巴斯夫 PA6 玻纖增強(qiáng)30% 耐油性 汽車(chē)部件Ultramid? B3WG6Polyamide 6BASF Corporation30% 玻璃纖維增強(qiáng)材料產(chǎn)品說(shuō)明：Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade.ApplicationsTypical applications include automotive manifolds and pedals.物性信息：基本信息黃卡編號(hào)E36632-531660E41871-233703填料/增強(qiáng)材料玻璃纖維增強(qiáng)材料, 30% 填料按重量添加劑熱穩(wěn)定劑特性耐油性能熱穩(wěn)定性用途汽車(chē)的發(fā)動(dòng)機(jī)罩下的零件汽車(chē)領(lǐng)域的應(yīng)用機(jī)構(gòu)評(píng)級(jí)EC 1907/2006 (REACH)RoHS 合規(guī)性RoHS 合規(guī)形式粒子加工方法注射成型多點(diǎn)數(shù)據(jù)Creep Modulus vs. Time (ISO 11403-1)Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)物理性能干燥調(diào)節(jié)后的單位制測(cè)試方法比重1.36--g/cm3ASTM D792, ISO 1183溶化體積流率（MVR） (275°C/5.0 kg)50.0--cm3/10minISO 1133收縮率 - 流動(dòng) (3.18 mm)0.30--%吸水率 飽和6.6--%ASTM D570 飽和, 23°C6.6--%ISO 62 平衡, 50% RH2.1--%ASTM D570 平衡, 23°C, 50% RH2.1--%ISO 62機(jī)械性能干燥調(diào)節(jié)后的單位制測(cè)試方法拉伸模量 (23°C)95006200MPaISO 527-2抗張強(qiáng)度 斷裂, 23°C179--MPaASTM D638 斷裂, 23°C185115MPaISO 527-2伸長(zhǎng)率 斷裂, 23°C3.3--%ASTM D638 斷裂, 23°C3.58.0%ISO 527-2彎曲模量 23°C8280--MPaASTM D790 23°C86005000MPaISO 178彎曲應(yīng)力 (23°C)270180MPaISO 178沖擊性能干燥調(diào)節(jié)后的單位制測(cè)試方法簡(jiǎn)支梁缺口沖擊強(qiáng)度ISO 179 -30°C11--kJ/m2ISO 179 23°C1530kJ/m2ISO 179簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度ISO 179 -30°C80--kJ/m2ISO 179 23°C95110kJ/m2ISO 179懸壁梁缺口沖擊強(qiáng)度 -40°C110--J/mASTM D256 23°C130--J/mASTM D256 23°C1520kJ/m2ISO 180熱性能干燥調(diào)節(jié)后的單位制測(cè)試方法載荷下熱變形溫度 0.45 MPa, 未退火220--°CASTM D648, ISO 75-2/B 1.8 MPa, 未退火207--°CASTM D648 1.8 MPa, 未退火210--°CISO 75-2/A熔融峰值溫度220--°CASTM D3418, ISO 3146